Incoloy 800 H / HT (UNS N08811) Fe base, Ni 32, Cr 21, Mn 1.5 Description


Ni 32.5 Cr 21 Mn 1.5 C 0.10 Si 1.0 Fe 39.5 Cu 0.75 S 0.015 Al 0.60 max. Ti 0.60 max

 

High Performance Alloys stocks and produces Incoloy 800 H in this grade in the following forms: Bar, sheet/plate, fasteners. Request quote on this grade.

 

  1. Download FDA statement concerning the use of stainless steels as food contact surfaces of equipment. 154 KB PDF

 

Overview

UNS N08810 / UNS N08811
Incoloy 8Incoloy 800 H is an iron-nickel-chromium alloy having the same basic composition as Incoloy 800, with significantly higher creep rupture strength. The higher strength results from close control of carbon, aluminum and titanium contents in conjunction with a high temp anneal. The 800H modification was to control carbon (0.05 to 0.10%) and grain size to (>ASTM 5) to optimize stress rupture properties. Incoloy 800 H has further modifications to the combined titanium and aluminum levels (0.85 to 1.2%) to ensure optimum high temperature properties. The alloy is dual certified and combines the properties of both forms.

The chemical balance allows the alloy to exhibit excellent resistance to carburization, oxidation and nitriding atmospheres. 800HT will not become embrittled even after long periods of usage in the 1200-1600 deg F range where many stainless steels become brittle. Excellent cold forming characteristics typically associated with the nickel-chromium alloys are exhibited with 800HT. When cold formed extensively the grain size produces a visibly undulated surface called "orange peel". 800HT can be welded by the common techniques used on stainless steels.

Typical applications for the alloy include ethylene pyrolysis, hydrocarbon cracking, cracking furnaces for vinyl chloride, diphenol and acetic acid. The alloy is also used for valves, fittings and other components exposed to corrosive attack from 1100 to 1800 deg F.

Round bar ranging from 3/4" to 6" diameter, and light gauge sheet and plate. Incoloy 800 H material can be supplied in random lengths, cut to order or machined to customer requirements. Machining includes drilling, threading, milling, CNC shapes, turning, tapping, flanges and others.

Chemistry

Chemical Requirements

Ni

Cr

Mn

C

Si

Fe

C

Max

35.0

23.0

1.5

0.10

1.0

0.75

Min

30.0

19.0

39.5


Tensile Data

Mechanical Property Requirements

Ultimate Tensile, min.

Yield Strength (0.2% OS)

Elong. in 2 in. or 50mm (or 4D) min., %

R/A

Hardness

Min

80 KSi

35 KSi

25

Max

Min

550 MPa

240 MPa

Max

 


Specifications

Form

Standard

Metal Type

UNS N08800 / N08810 / N08811

Bar

ASTM B408

Wire

Sheet

ASTM B409

Plate

ASTM B409

Fitting

ASTM B366

Forging

ASTM B564

Weld Wire

 

Weld Electrode

 


Machining

MACHINING DATA
Carbide tools are suggested
for rates better than 50% of Type 304.
Machining Type Suggested starting rates are:
Single Point turning : Roughing - 0.15" depth, 0.015"/rev feed -175 SFM
Finishing - 0.025" depth, 0.007"/rev feed - 200 SFM
Drilling : 1/4" Dia hole - 0.004"/rev feed - 60 SFM
1/2" Dia hole - 0.007"/rev feed - 60 SFM
3/4" Dia hole - 0.010"/rev feed - 60 SFM
Reaming : Feed - same as drilling - 100 SFM
Side and Slot Milling : Roughing - 0.25" depth - 0.007"/tooth feed - 125SFM
Finishing - 0.050" depth - 0.009"/tooth feed - 140SFM
These rates are for carbide tools,
Type C-2 for roughing, drilling and reaming.
Type C-3 for finishing.

 


INCOLOY® is a registered trademark of the INCO family of companies.



<